China Manufacturer Special Steel High Quality Stainless Steel 15-5PH Bar
Standard:JIS, AISI, ASTM, GB, DIN, EN
Length: 1000~6000mm, or by customized.
MOQ: 0.5 Ton
- Inquiry
Model: 15-5PH / S15500 / XM-12 / W.Nr.1.4545
Introduction:
15-5PH is a martensitic precipitation-hardening stainless steel that provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600F (316C) and good toughness in both the longitudinal and transverse directions in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling.
15-5PH is the ferrite-free version of 17-4PH Stainless Steel. Both alloys are widely used in theaerospace, chemical, petrochemical, food processing, paper and general metalworking industries.
Similar Grades:DIN 1.4545, UNS S15500, 15-5PH
15-5PH is the ferrite-free version of 17-4PH Stainless Steel. Both alloys are widely used in theaerospace, chemical, petrochemical, food processing, paper and general metalworking industries.
Similar Grades:DIN 1.4545, UNS S15500, 15-5PH
Shape:Round, Flat, Square.
Size Range:
Diameter(mm) | Thickness (mm) | Width (mm) | Length(mm) | |
Round | 20-480 | - | - | 2000-5800 |
Square | 20-480 | - | - | 2000-5800 |
flat | - | 20-50 | 80-600 | 2000-5800 |
Steel-making Condition:
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Chemical Composition:
C | Mn | P | S | Si | Cr | Ni | Cu | Nb+Ta |
0.07max | 1.0max | 0.030max | 0.035max | 1.0max | 14.0-15.0 | 3.5-5.5 | 2.5-4.5 | 0.15-0.45 |
Mechanical Properties
Delivey Condition | Moduls of Elasticity(GPa) | Moduls of Rigidity(GPa) | Tensile Strength Rm (Mpa) | Yield Strength Rp0.2 (Mpa) | Elongation % in 2″ (50.8 mm) | Reduction Of Area (%) | Hardness (HRC) |
A(annealed) | / | / | / | / | / | / | 35 max |
H 900 | 197.6 | 77.3 | 1378 min | 1276 min | 14 min | 50min | 44min |
H925 | / | / | 1309 min | 1207 min | 14 min | 54min | 42min |
H1025 | / | 75.9 | 1173 min | 1138 min | 15 min | 56min | 38min |
H1075 | / | 69 | 1138 min | 1035 min | 16 min | 58min | 36min |
H1100 | / | / | 1035 min | 931 min | 17 min | 58min | 34min |
H1150 | / | 69 | 1000 min | 862 min | 19 min | 60min | 33min |