China Factory Special Steel Nickel Alloy High Quality Inconel 600 for Environmental

Inconel 600 is a nickel-chromium alloy used for applications that require corrosion and high temperature resistance. This nickel alloy was designed for service temperatures from cryogenic to elevated temperatures in the range of 2000° F. It is non-magnetic, has excellent mechanical properties, and presents the desirable combination of high strength and good weldability under a wide range of temperatures.
Alloy 600 can be both hot formed and cold formed using typical processes. Hot working should be performed between 1600° F and 2250° F avoiding any work between1200-1600° F because the ductility decreases in this temperature range. Welding Alloy 600 can be achieved via shielded metal-arc welding, TIG, and MIG.
1.Resistant to a wide range of corrosive media. 2.Virtually immune to chlorine ion stress corrosion cracking.3.Non-magnetic 4.Excellent mechanical properties 5.High strength and good weldability under a wide range of temperatures

  • Product Description
  • Inquiry

Model: Inconel Alloy 600
Brand: Ronsco
Code: Alloy1996inconel600

Ronsco ALLOY 600 PARAMETER TABLE

Inconel® Alloy 600,UNS N06600, DIN W.Nr.2.4816, NC15Fe , NiCr15Fe, NA14, NiCr15Fe8
Genenal Introduction
Alloy 600 is a nickel-chromium-iron, solid solution strengthened alloy with good oxidation resistance at higher temperatures, with good resistance in carburizing and chloride containing environments.This alloy also displays good heat resistance and freedom from aging or stress corrosion throughout the annealed to heavily cold worked condition range.

Alloy 600 is non-magnetic, has excellent mechanical properties and a combination of high strength and good workability and is readily weldable. Inconel® Alloy 600 exhibits cold forming characteristics normally associated with chromium-nickel stainless steels.
Chemical Composition:
ContentCNiCrFeSiMnSCu
Min--72.0 14.0 6.0 --------
Max0.1 --17.0 10.0 0.5 1.0 0.015 0.5 
Forms & Standard
FormStandardFormStandard
BarASTM B166 AMS 5665 Din 17752SheetASTM B168 AMS 5540 Din 17750
PlateASTM B168 AMS 5540 Din 17750TubeASTM B167
PipeASTM B167FittingASTM B366
ForgingASTM B564 Din 17754Weld WireFM 82/ ERNiCr-3
Weld ElectrodeFM 182/ ENiCrFe-3

Average Physical Properties
Physical Properties°FBritish Units°CMetric Units
DensityRoom0.304 lb./cubic in.Room8.43g/cubic cm
Electrical
Resistivity
7040.6 microhm-in.211.03 microhm-m
20040.9931.04
40041.52041.05
60042.23161.07
80043.0 4271.09
Mean Coefficient
of Thermal
Expansion
70-2007.4 microinches/in.-°F21-9313.3 x 10(-6)m/m·K
70-4007.721-20413.9
70-6007.921-31614.2
70-8008.121-42714.6
Thermal
Conductivity
70103 Btn-in./ft².-hr.-°F2114.8 W/m·K
2001099315.7
40012120417.4
60013331619.2
80014542720.9
Modulus
of Elasticity
Room30.0 x 10(6) psiRoom207 GPa
Typical Mechanical Properties:
Form and ConditionTensile StrengthYield Strength
0.2%
 Elongation
in 2" %
Reduction
of Area %
Rockwell
Hardness
BarAnnealed80-100552-68925-50172-34555-3570-6065-85B
As-drawn105-150724-103480-125552-8624376860-3090B-30C
Hot rolled






Annealed80-100552-68930-50207-34555-3570-6065-85B
As-rolled85-120586-82735-90241-62150-3065-5075-95B
Hot-finished80-120586-82735-90241-62150-3065-5075-95B
StripAnnealed80-100552-68930-45207-31055-35----84B max.
SheetAnnealed986764229040--------
PlateAnnealed956554128345--------
Bar/BilletAnnealed956554128345--------
Sheet, Plate, Strip, BarAnnealed805503524030--------
Applications
Barge and tank truck linersCarburizing atmospheres
Ethylene dichloride crackersFurnace trays, mufflers, hangers
Gasoline stabilizer productionMgCl2 evaporates
Phenol condensersSoap manufacture
Titanium dioxideVegetable and fatty acid vessels
Resistance to Corrosion
With 72% minimum nickel, this alloy is resistant to many organic and inorganic compounds and also offers good corrosion resistance in reducing conditions. The high nickel content lowers the chances for stress corrosion cracking for this alloy in the annealed condition. The high nickel content also improves resistance to carburizing, nitriding and thermal fatigue, while maintaining an austenitic structure so it retains ductility. Increased chromium in the alloy offers high temperature resistance to sulfur compounds as well as resistance to oxidizing compounds at elevated temperatures or in corrosive media. Alloy 600 has excellent resistance to alkalies and is one of the few materials suitable for use in strong solutions of magnesium chloride at elevated temperatures. Typical corrosion in MgCl₂ is roughly 1 mpy. When applicable, material for severe service should be fully stress relieved prior to use.
Fabrication and Heat Treatment
Alloy 600 can be hot or cold formed using typical processes. Hot working should be performed between 1600°F and 2250°F, avoiding any work between 1200°F and 1600°F as the ductility decreases in this temperature range. The cold work hardening rate is less than 304 stainless steel yet higher than mild steel. Welding alloy 600 can be achieved via shielded metal-arc welding using AWS ENiCrFe-3 electrode. Filler metal AWS ERNiCr-3 can be used when TIG and MIG welding. Alloy 600 is slightly more machinable compared to 304 stainless steel and should be performed with tooling large enough to handle the loads. Alloy 600 machining requires heavy-duty equipment along with sharp tooling and proper cutting fluids. Annealing of alloy 600 without excessive grain growth can be performed at 1850°F for 15 minutes at temperature. Fine grain material typically has better corrosion resistance and higher tensile, fatigue and impact properties.
The advantage of Ronsco
1, Price lower than Europe, USA 20~30%.
2, 100% quality guaranty because we remelt by VIM+ESR.
3, Best Service: 0 payment if you test not ok. 
4, 0 fee for UT, PT.               
5, Low MOQ for new materials: 200kg.
6, Fast 20~30 days of lead time for new materials.


For More Information About Inconel Alloy 600, please call +86 17708476248 or Send an Email to [[email protected]]