Hastelloy C276 Round Bar is a nickel-iron- chromium alloy with titanium, copper, and molybdenum. Hastelloy C276 Round Bar composition provides great resistance to many corrosive environments, such as pitting, crevice corrosion, intergranular corrosion, and stress- corrosion cracking.
Hastelloy C276 Specification:
Grade | Hastelloy Alloy C276 / UNS N10276 / Werkstoff Nr. 2.4819 |
Specification | EN, DIN, JIS, ASTM, BS, ASME, AISI |
Standard | ASTM B574 / ASME SB574 |
Size | 5 mm To 500 mm |
Diameter | 0.1 mm to 100 mm |
Length | 100 mm To 3000 mm Long & Above |
Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
STANDARD | WERKSTOFF NR. | UNS | JIS | EN | GOST | OR |
Hastelloy C276 | 2.4819 | N10276 | NW 0276 | NiMo16Cr15W | ХН65МВУ | ЭП760 |
Grade | C | Mn | Si | Co | P | Fe | Mo | Ni | Cr | S | W | V |
Hastelloy C276 | 0.010 max | 1 max | 0.08 max | 2.5 max | 0.04 max | 4 – 7 | 15 – 17 | Bal | 14.5-16.5 | 0.03 max | 3.0-4.5 | 0.35 max |
Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
8.89 g/cm3 | 1370 °C (2500 °F) | Psi – 1,15,000 , MPa – 790 | Psi – 52000 , MPa – 355 | 40% |
Most commonly used in petroleum refineries, Boilers, Heat exchangers, Condensers, Pipelines, Cooling towers, Steam exhausts, Electric generation plants, On occasion will be found in fertilizer and chemical plants.
Fabrication with Hastelloy C-276:
Hastelloy C-276 alloy can be forged, hot-upset and impact extruded. Although the alloy tends to work-harden, you can have it successfully spun, deep-drawn, press formed or punched. All of the common methods of welding can be used, although the oxyacetylene and submerged arc processes are not recommended when the fabricated item is for use in corrosion service.
Want to Learn More About Hastelloy C-276 Forged Round Bar Stockists、Price & Ronsco Forged Nickel Alloys Services;